Temper Embrittlement Tendency of 2~1/₄Cr-1Mo Steel Welding Joint in Hydrogen Atmospheret

杨权，赵卫君，申雷，王兆民

哈尔滨锅炉厂有限责任公司

摘　要

采用步冷试验法对21/4Cr-1Mo钢焊接接头的回火脆化倾向性进行评定试验。结果表明,由于焊缝、焊缝金属的回火脆化倾向性,试验焊接接头焊接热影响区的韧性高于焊接热影响区。由于焊缝和母材的磷含量较低,磷偏聚对回火脆化倾向性的影响较小,而组织结构对韧性和回火脆化倾向性的影响较大。

关键词

铬钼钢；回火脆化；步冷试验；热处理

分类号

TG407

栏　目

试验研究

出　处

《冶金与材料》2015年第2期，第 8-10+14 页（共 4 页）

出版日期

2015-04-15

知网数据

下载 105 次（截至 2026-09-29）

Abstract

Test study of temper embrittlement tendency for welding joint of 2Cr- 1Mo steel is carried out using step cooling test method. The results show that,due to the tendency of temper embrittlement of weld metal,the toughness of the heat affected zone of test welded joint is higher than that of heat affected zone. Because the phosphorus content in the weld and base material is lower,so phosphorus segregation effect on temper embrittlement tendency is smaller,while the affect of structure on toughness and embrittlement is si gnifican.

Keywords

Cr-Mo steel; temper embrittlement; step-cooling test; heat treatment

知网全文（电脑版） 知网公开页

“知网全文（电脑版）”需登录中国知网或在已订购知网的机构 IP 内访问；“知网公开页”无需登录即可查看摘要，并可按知网规定下载全文。